Texture (crystalline)

In materials science, texture is the distribution of crystallographic orientations of a polycrystalline sample. A sample in which these orientations are fully random is said to have no texture. If the crystallographic orientations are not random, but have some preferred orientation, then the sample has a weak, moderate or strong texture. The degree is dependent on the percentage of crystals having the preferred orientation. Texture is seen in almost all engineered materials, and can have a great influence on material properties. Also, geologic rocks show texture due to their thermo-mechanic history of formation processes.

One extreme case is a complete lack of texture: a solid with perfectly random crystallite orientation will have isotropic properties at length scales sufficiently larger than the size of the crystallites. The opposite extreme is a perfect single crystal, which has anisotropic properties by geometric necessity.

Contents

Characterization and representation

Texture can be determined by various methods.[1] Some of them allow a quantitative analysis of the texture; others are only qualitative. Among the quantitative techniques, the most widely used is X-ray diffraction using texture goniometers, followed by EBSD-method (electron backscatter diffraction) in Scanning Electron Microscopes. Qualitative analysis can be done by Laue photography, simple X-ray diffraction or with the polarized microscope. Neutron and synchrotron high-energy X-ray diffraction allow access to textures of bulk material and in-situ analysis, whereas laboratory x-ray diffraction instruments are more appropriate for thin film textures.

Texture is often represented using a pole figure, in which a specified crystallographic axis (or pole) from each of a representative number of crystallites is plotted in a stereographic projection, along with directions relevant to the material's processing history. These directions define the so-called sample reference frame and are, because the investigation of textures started from the cold working of metals, usually referred to as the rolling direction RD, the transverse direction TD and the normal direction ND. For drawn metal wires the cylindrical fiber axis turned out as the sample direction around which preferred orientation is typically observed (see below).

Common Textures

There are several textures that are commonly found in processed materials. They are named either by the scientist that discovered them, or by the material they are most found in. These are given in miller indices for simplification purposes.

  • Cube component: (001)[100]
  • Brass component: (110)[-112]
  • Copper component: (112)[11-1]
  • S component: (123)[63-4]

Orientation distribution function

The full 3D representation of crystallographic texture is given by the orientation distribution function (ODF) which can be achieved through evaluation of a set of pole figures or diffraction spectra. Subsequently, all pole figures can be derived from the ODF.

The ODF is defined as the volume fraction of grains with a certain orientation \boldsymbol{g}.

ODF(\boldsymbol{g})=\frac{1}{V} \frac{dV(\boldsymbol{g})}{d g}.

The orientation \boldsymbol{g} is normally identified using three Euler angles. The Euler angles then describe the transition from the sample’s reference frame into the crystallographic reference frame of each individual grain of the polycrystal. One thus ends up with a large set of different Euler angles, the distribution of which is described by the ODF.

The orientation distribution function, ODF, cannot be measured directly by any technique. Traditionally both X-ray diffraction and EBSD may collect pole figures. Different methodologies exist to obtain the ODF from the pole figures or data in general. They can be classified based on how they represent the ODF. Some represent the ODF as a function, sum of functions or expand it in a series of harmonic functions. Others, known as discrete methods, divide the ODF space in cells and focus on determining the value of the ODF in each cell.

Origins

Scan of sectioned, forged connecting rod that has been etched to show grain flow.

In wire and fiber, all crystals tend to have nearly identical orientation in the axial direction, but nearly random radial orientation. The most familiar exceptions to this rule are fiberglass, which has no crystal structure, and carbon fiber, in which the crystalline anisotropy is so great that a good-quality filament will be a distorted single crystal with approximately cylindrical symmetry (often compared to a jelly roll). Single-crystal fibers are also not uncommon.

The making of metal sheet often involves compression in one direction and, in efficient rolling operations, tension in another, which can orient crystallites in both axes by a process known as grain flow. However, cold work destroys much of the crystalline order, and the new crystallites that arise with annealing usually have a different texture. Control of texture is extremely important in the making of silicon steel sheet for transformer cores (to reduce magnetic hysteresis) and of aluminium cans (since deep drawing requires extreme and relatively uniform plasticity).

Texture in ceramics usually arises because the crystallites in a slurry have shapes that depend on crystalline orientation, often needle- or plate-shaped. These particles align themselves as water leaves the slurry, or as clay is formed.

Casting or other fluid-to-solid transitions (i.e., thin-film deposition) produce textured solids when there is enough time and activation energy for atoms to find places in existing crystals, rather than condensing as an amorphous solid or starting new crystals of random orientation. Some facets of a crystal (often the close-packed planes) grow more rapidly than others, and the crystallites for which one of these planes faces in the direction of growth will usually out-compete crystals in other orientations. In the extreme, only one crystal will survive after a certain length: this is exploited in the Czochralski process (unless a seed crystal is used) and in the casting of turbine blades and other creep-sensitive parts.

Texture and Materials Properties

Material properties such as strength,[2] chemical reactivity,[3] stress corrosion cracking resistance,[4] weldability,[5] deformation behavior[2][3], resistance to radiation damage, [6] [7] and magnetic susceptibility[8] can be highly dependent on the material’s texture and related changes in microstructure. In many materials, properties are texture-specific, and development of unfavorable textures when the material is fabricated or in use can create weaknesses that can initiate or exacerbate failures.[2][3] Parts can fail to perform due to unfavorable textures in their component materials.[3][8] Failures can correlate with the crystalline textures formed during fabrication or use of that component.[2][5]. Consequently, consideration of textures that are present in and that could form in engineered components while in use can be a critical when making decisions about the selection of some materials and methods employed to manufacture parts with those materials.[2][5] When parts fail during use or abuse, understanding the textures that occur within those parts can be crucial to meaningful interpretation of failure analysis data.[2][3]

Thin film textures

Pronounced textures occur in thin films. Modern technological devices to a large extent rely on polycrystalline thin films with thickness in the nanometer and micrometer range. This holds, for instance, for all microelectronic and most optoelectronic systems or sensoric and superconducting layers. Most thin film textures may be categorized into two different types: (1) for so-called fiber textures the orientation of a certain lattice plane is preferentially parallel to the substrate plane. (2) In contrast, in biaxial textures also the in-plane orientation of crystallites becomes locked with respect to the sample. The latter phenomenon is accordingly observed in nearly epitaxial growth processes, where the crystallographic axes of the layer tend to align along those of the substrate.

Tailoring the texture on demand became an important task in thin film technology. In the case of oxide compounds intended for transparent conducting films or surface acoustic wave (SAW) devices, for instance, the polar axis should be aligned along the substrate normal.[9] Another example is given by cables from high-temperature superconductors that are being developed as oxide multilayer systems deposited on metallic ribbons.[10] The adjustment of the biaxial texture in YBa2Cu3O7 layers turned out as the decisive prerequisite for achieving sufficiently large critical currents.[11]

The degree of texture is often subjected to an evolution during thin film growth [12] and that most pronounced textures are only obtained after the layer has achieved a certain thickness. Thin film growers thus require information about the texture profile or the texture gradient in order to optimize the deposition process. The determination of texture gradients by x-ray scattering, however, is not straightforward, because different depths of a specimen contribute to the signal. Techniques that allow for the adequate deconvolution of diffraction intensity were developed only recently.[13][14]

References

  1. ^ H.-R. Wenk and P. Van Houtte (2004). "Texture and anisotropy". Rep. Progr. Phys. 67: 1367–1428. Bibcode 2004RPPh...67.1367W. doi:10.1088/0034-4885/67/8/R02. 
  2. ^ a b c d e f O. Engler and V. Randle (2009). Introduction to Texture Analysis: Macrotexture, Microtexture, and Orientation Mapping, Second Edition. CRC Press. ISBN 978-1420063653. 
  3. ^ a b c d e U. F. Kocks, C. N. Tomé, H. -R. Wenk and H. Mecking (2000.). Texture and Anisotropy: Preferred Orientations in Polycrystals and their effects on Materials Properties.. Cambridge University Press.. ISBN 978-0521794206.. 
  4. ^ D. B. Knorr, J. M. Peltier, and R. M. Pelloux, "Influence of Crystallographic Texture and Test Temperature on Initiation and Propagation of Iodine Stress-Corrosion Cracks in Zircaloy", (1972). Zirconium in the Nuclear Industry: Sixth International Symposium. Philadelphia, PA: ASTM. pp. 627-651. 
  5. ^ a b c Peter Rudling, A. Strasser, and F. Garzarolli. (2007). Welding of Zirconium Alloys. Sweden: Advanced Nuclear Technology International. pp. 4-3(4-13). http://www.antinternational.com/fileadmin/Products_and_handbooks/IZNA/First_chapter_IZNA_7_STR_Weld.pdf. 
  6. ^ Y. S. Kim, H. K. Woo, K. S. Im, and S. I. Kwun (2002). "The Cause for Enhanced Corrosion of Zirconium Alloys by Hydrides". Zirconium in the Nuclear Industry: Thirteenth International Symposium. (Philadelphia, PA: ASTM): 277. ISBN 978-0803128958. 
  7. ^ Brachet J., Portier L., Forgeron T., Hivroz J., Hamon D., Guilbert T., Bredel T., Yvon P., Mardon J., Jacques P. (2002). "Influence of Hydrogen Content on the α/β Phase Transformation Temperatures and on the Thermal-Mechanical Behavior of Zy-4, M4 (ZrSnFeV), and M5™ (ZrNbO) Alloys During the First Phase of LOCA Transient". Zirconium in the Nuclear Industry: Thirteenth International Symposium. (Philadelphia, PA: ASTM): 685. ISBN 978-0803128958. 
  8. ^ a b B. C. Cullity (1956). Elements of X-Ray Diffraction. United States of America: Addison-Wesley. pp. 273-274. 
  9. ^ M. Birkholz, B. Selle, F. Fenske and W. Fuhs (2003). "Structure-Function Relationship between Preferred Orientation of Crystallites and Electrical Resistivity in Thin Polycrystalline ZnO:Al Films". Phys. Rev. B 68: 205414. Bibcode 2003PhRvB..68t5414B. doi:10.1103/PhysRevB.68.205414. 
  10. ^ A. Goyal, M. Parans Paranthaman and U. Schoop (2004). "The RABiTS Approach: Using Rolling-Assisted Biaxially Textured Substrates for High-Performance YBCO Superconductors". MRS Bull. 29 (august): 552–561. 
  11. ^ Y. Iijima, K. Kakimoto, Y. Yamada, T. Izumi, T. Saitoh and Y. Shiohara (2004). "Research and Development of Biaxially Textured IBAD-GZO Templates for Coated Superconductors". MRS Bull. 29 (august): 564–571. 
  12. ^ A. van der Drift (1967). "Evolutionary selection, a principle governing growth orientation in vapor-deposited layers". Phil. Res. Rep. 22: 267–288. 
  13. ^ J. Bonarski (2006). "X-ray texture tomography of near-surface areas". Progr. Mat. Sc. 51: 61–149. doi:10.1016/j.pmatsci.2005.05.001. 
  14. ^ M. Birkholz (2007). "Modelling of diffraction from fiber texture gradients in thin polycrystalline films". J. Appl. Cryst. 40: 735–742. doi:10.1107/S0021889807027240. 

Further reading

  • Bunge, H.-J. "Mathematische Methoden der Texturanalyse" (1969) Akademie-Verlag, Berlin
  • Bunge, H.-J. "Texture Analysis in Materials Science" (1983) Butterworth, London
  • Kocks, U. F., Tomé, C. N., Wenk, H.-R., Beaudoin, A. J., Mecking, H. "Texture and Anisotropy – Preferred Orientations in Polycrystals and Their Effect on Materials Properties" (2000) Cambridge University Press ISBN 052179420X
  • Birkholz, M., chapter 5 of "Thin Film Analysis by X-ray Scattering" (2006) Wiley-VCH, Weinheim ISBN 3-527-31052-5

External links


Wikimedia Foundation. 2010.

Look at other dictionaries:

  • Texture — refers to the properties held and sensations caused by the external surface of objects received through the sense of touch. Texture is sometimes used to describe the feel of non tactile sensations. Texture can also be termed as a pattern that has …   Wikipedia

  • Crystalline — Crys tal*line (kr?s tal l?n or l?n; 277), a. [L. crystallinus, from Gr. ????: cf. F. cristallin. See {Crystal}.] 1. Consisting, or made, of crystal. [1913 Webster] Mount, eagle, to my palace crystalline. Shak. [1913 Webster] 2. Formed by… …   The Collaborative International Dictionary of English

  • Crystalline heavens — Crystalline Crys tal*line (kr?s tal l?n or l?n; 277), a. [L. crystallinus, from Gr. ????: cf. F. cristallin. See {Crystal}.] 1. Consisting, or made, of crystal. [1913 Webster] Mount, eagle, to my palace crystalline. Shak. [1913 Webster] 2. Formed …   The Collaborative International Dictionary of English

  • Crystalline lens — Crystalline Crys tal*line (kr?s tal l?n or l?n; 277), a. [L. crystallinus, from Gr. ????: cf. F. cristallin. See {Crystal}.] 1. Consisting, or made, of crystal. [1913 Webster] Mount, eagle, to my palace crystalline. Shak. [1913 Webster] 2. Formed …   The Collaborative International Dictionary of English

  • Crystalline spheres — Crystalline Crys tal*line (kr?s tal l?n or l?n; 277), a. [L. crystallinus, from Gr. ????: cf. F. cristallin. See {Crystal}.] 1. Consisting, or made, of crystal. [1913 Webster] Mount, eagle, to my palace crystalline. Shak. [1913 Webster] 2. Formed …   The Collaborative International Dictionary of English

  • Micrographic texture — In petrology, micrographic texture is a fine grained intergrowth of quartz and alkali feldspar, interpreted as the last product of crystallization in some igneous rocks which contain high or moderately high percentages of silica. Micropegmatite… …   Wikipedia

  • sedimentary rock — Rock formed at or near the Earth s surface by the accumulation and lithification of fragments of preexisting rocks or by precipitation from solution at normal surface temperatures. Sedimentary rocks can be formed only where sediments are… …   Universalium

  • igneous rock — Any of various crystalline or glassy, noncrystalline rocks formed by the cooling and solidification of molten earth material (magma). Igneous rocks comprise one of the three principal classes of rocks, the others being metamorphic and sedimentary …   Universalium

  • soil — soil1 soilless, adj. /soyl/, n. 1. the portion of the earth s surface consisting of disintegrated rock and humus. 2. a particular kind of earth: sandy soil. 3. the ground as producing vegetation or as cultivated for its crops: fertile soil. 4. a… …   Universalium

  • Volcanic rock — is an igneous rock of volcanic origin. Texture Volcanic rocks are usually fine grained or aphanitic to glassy in texture. They often contain clasts of other rocks and phenocrysts. Phenocrysts are crystals that are larger than the matrix and are… …   Wikipedia


Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”

We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.