Compact disc manufacturing
Compact disc manufacturing is the process by which commercial
compact discs (CDs) are replicated in mass quantities using a master version created from a source recording. This may be either in audio form ( CD-Audio) or data form ( CD-ROM). This process is used in the mastering of CDs; CD-Rs, CD-RWs, and DVDs, are made somewhat differently, though the methods are broadly similar.
A compact disc (CD) can be used to store
audio, video, and data in various standardized formats defined in the Rainbow Books. CDs are usually manufactured in a class 100 or better clean room; they can usually be manufactured to quite strict manufacturing tolerances for only a few US cents per disk.
CD mastering differs from burning, as the pits and lands of a mastered CD are moulded into a CD blank, rather than being 'burn marks' in a dye layer (in CD-Rs) or areas with changed physical characteristics (in CD-RWs). In addition,
CD burners write data sequentially, while a CD pressing plant 'writes' the entire disk in one physical stamping operation.
All CDs are pressed from a
digitaldata source, with the most common sources being low error-rate CD-Rs or files from an attached computer hard drivecontaining the finished data (eg, music or computer data (ie, programs, etc)). Some CD pressing systems can use digitalmaster tapes, either in Digital Audio Tape, Exabyteor Umaticformats. However such sources are suitable only for production of audio CDs due to error detection and correction issues. If the source is not a CD, the table of contentsfor the CD to be pressed must also be prepared and stored on the tape or hard drive. In all cases except CD-Rsources, the tape must be uploaded to a media mastering system to create the TOC (Table Of Contents) for the CD.
Glassmastering is performed in a class 100 or better clean roomor a self-enclosed clean environment within the mastering system. Contaminants introduced during critical stages of manufacturing (eg, dust, pollen, hair, or smoke) can cause sufficient errors to make a master unusable. Once successfully completed, a CD master will be less susceptible to the effects of these contaminants.
During glass mastering, glass is used as a substrate to hold the CD master image while it is created and processed; hence the name. Glass substrates, noticeably larger than a CD, are round plates of glass approximately 240 mm in diameter and 6 mm thick. They often also have a small,
steelhub on one side to facilitate handling. The substrates are created specially for CD mastering and one side is polished until it is extremely smooth. Even microscopic scratches in the glass will affect the quality of CDs pressed from the master image. The extra area on the substrate allows for easier handling of the glass master and reduces risk of damage to the pit and land structure when the "father" stamper is removed from the glass substrate.
Once the glass substrate is cleaned using
detergentsand ultrasonic baths, the glass is placed in a spin coater. The spin coater rinses the glass black with a solventand then applies either photoresist or dye-polymer depending on the mastering process. Rotation spreads the photoresist or dye-polymer coating evenly across the surface of the glass. The substrate is removed and baked to dry the coating and the glass substrate is ready for mastering.
Mastering is performed by a
Laser Beam Recorder(LBR) machine. These use one of two recording techniques; photo resist and non-photoresist mastering. Photoresist also comes in two variations; positive photoresist and negative photoresist.
While nearly all mastering to glass is done at multiple speeds for sake of plant efficiency (8X or higher is common), single speed glass mastering (also referred to as 1X glass cutting or 1x glass mastering) is offered by a few CD replication plants as a higher quality process. A large number of audiophiles believe this results in truer reproduction although this has remained a matter of controversy for many years.
Photoresist mastering uses a light-sensitive material (a
photoresist) to create the pits and lands on the CD master blank.
The laser beam recorder uses a deep blue or
ultraviolet laserto write the master. When exposed to the laser light, the photoresist undergoes a chemical reaction which hardens it. The exposed area is then soaked in a developer solution which removes the exposed positive photoresist or the unexposed negative photoresist.
Once the mastering is complete, the glass master is removed from the LBR and chemically 'developed'.
Once developing is finshed, the glass master is metalized to provide a surface for the stamper to be formed onto.
Non-photoresist (NPR) or Dye-Polymer mastering
Once the glass is ready for mastering, it is placed in a Laser Beam Recorder (LBR). Most LBRs are capable of mastering at greater than x1 speed, but due to the weight of the glass substrate and the requirements of a CD master they are typically mastered at no greater than 8X playback speed. The LBR uses a laser to write the information, with a wavelength and final lens NA (numerical aperture) chosen to produce the required pit size on the master blank. For example, DVD pits are smaller than CD pits, so a shorter wavelength or higher NA (or both) is needed for DVD mastering.
When a laser is used to record on the dye-polymer used in NPR mastering, the dye-polymer absorbs laser energy focused in a precise spot; this vapourises and forms a pit in the surface of the dye-polymer. This pit can be scanned by a red laser beam that follows the cutting beam, and the quality of the recording can be directly and immediately assessed; for instance, audio signals being recorded can also be played straight from the glass master in real time. The pit geometry and quality of the playback can all be adjusted while the CD is being mastered, as the blue writing laser and the red read laser are typically connected via a feedback system to optimise the recording. This allows the dye-polymer LBR to produce very consistent pits even if there are variations in the dye-polymer layer. Another advantage of this method is that pit depth variation can be programmed during recording to compensate for downstream characteristics of the local production process (eg, marginal molding performance). This cannot be done with photoresist mastering because the pit depth is set by the PR coating thickness, whereas dye-polymer pits are cut into a coating thicker than the intended pits.
This type of mastering is called "Direct Read After Write" or "DRAW" and is the main advantage of some non-photoresist recording systems. Problems with the quality of the glass blank master, such as scratches, or an uneven dye-polymer coating, can be immediately detected. If required the mastering can be halted, saving time and increasing throughput.
After mastering, the glass master is baked to harden the developed surface material to prepare it for metalisation. Metalisation is a critical step prior to electrogalvanic manufacture (
The developed glass master is placed in a
vapour depositionmetaliser which uses a combination of mechanical vacuum pumps and cryopumps to lower the total vapour pressure inside a chamber to a hard vacuum. A piece of nickelwire is then heated in a tungsten boatto white hot temperature and the nickel vapour deposited onto the rotating glass master. The glass master is coated with the nickel vapour up to a typical thickness of around 400nm.
The finished glass masters are inspected for stains, pinholes or incomplete coverage of the nickel coating and passed to the next step in the mastering process.
Electroformingoccurs in "Matrix", the name used for the electroforming process area in many plants; it is also a class 100 cleanroom. The data (music, computer data, etc) on the metalised glass master is extremely easy to damage and must be transferred to a tougher form for use in the injection moulding equipment which actually produces the end-procut optical disks.
The metalised master is clamped in a conductive plating frame with the data side facing outwards and lowered into a plating tank. The tank contains a
nickel saltsolution (usually nickel sulfamate) at a particular concentration which may be adjusted slightly in different plants depending on the characteristics of the prior steps. The solution is carefully buffered to maintain its pH, and detergents are added to maintain a specific surface tension. If the surface tension is too high, the solution cannot flow around the very small features (ie, the pits and lands) on the surface of the glass master sufficiently well to deposit metal properly. The bath is heated to approximately 40 °C.
The glass master is rotated in the plating tank while a pump circulates the plating solution over the surface of the master. As the electroforming progresses, nickel is galvanically drawn out of the solution and must be replenished to maintain a constant concentration in the plating bath. This is achieved using high purity nickel pellets (99.99% pure) suspended in the solution in non-conductive
polypropylenebags called " anodebags". The plating solution flows through the bag and over the glass master. The anode bags stop sediment formed during the nickel decomposition from reaching the solution and perhaps being plated onto to a master's surface. The nickel is packed firmly into the bag and forms part of the electric circuit.
DC currentapplied to the glass master is the source of the galvanic potential which forces nickel from the anode pellets in the bags into solution as ions and ultimately onto the master's surface as an electrically neutral metallic layer. The electrons flow in the opposite direction to the current, from the cathodeto the anode via the solution. Electrons are stripped from the nickel in the anode bag, travel through the external circuit before combining with nickel ions in the solution at the cathode end thus forming metallic nickel on the surface of the glass master.
The current must start off quite low and be increased slowly and evenly to prevent the metalised surface from overheating damage. As the thickness of the nickel on the glass master increases, the current can be increased. The electroplating step is finished after approximately 1 hour. Typical stampers are 0.300 mm thick. The part is removed from the tank and the metal layer peeled off the glass substrate. The metal part, now called a "father", has the desired data as a series of bumps rather than pits; it is a negative master. The father is washed with deionised water and other chemicals such as
sodium hydroxideor acetoneto remove all trace of resist or other contaminants. The glass master can be sent for reclamation, cleaning and checking before reuse. If defects are detected, it will be discarded or recycled.
Once cleaned of any loose nickel and resist, the father is
electrolysed, washed and clampedback into a frame and returned to the plating tank. This time the metal part that is grown is the mirror image of the father and is called a "mother"; this is a 'positive' master. All the stampers used to manufacture the CDs are made from a mother. Mothers can sometimes be regrown from fathers if they become damaged, however if handled correctly, 10 - 20 stampers can be grown from a single mother before the quality of the stamper is reduced unacceptably. Mothers are regrown from the father if it still exists, otherwise a new glass master is made.
If the CD is to be part of a long production run, the father may be
archived, however it is generally cut down with a hyper-accurate hydraulicpunch and used as a stamper for moulding runs. Stampers and fathers are the same (negative) "polarity", the information surface is made up of a series of bumps. Mothers are the reverse and have pits on their surfaces.
A father, mother, and a collection of stampers (sometimes called "sons") are known collectively as a "family". Fathers and mothers are the same size as a glass substrate, typically 300 μm in thickness. Stampers do not require the extra space around the outside of the program area and they are punched to remove the excess nickel from outside and inside the information area in order to fit the mould of the injection moulding machine (IMM). The physical dimensions of the mould vary somewhat from machine to machine.
CD moulding machines are specifically designed high temperature
polycarbonateinjection moulders. They have an average throughput of 550-900 discs per hour, per moulding line. Clear polycarbonate pellets are first dried at around 130 degrees Celsius for three hours (nominal; this depends on which optical grade resin is in use) and are fed via vacuum transport into one end of the injection moulder's barrel (ie, the feed throat) and are moved to the injection chamber via a large screw inside the barrel. The barrel, wrapped with heater bands ranging in temperature from ca 210 to 320 degrees Celsius melts the polycarbonate. When the mould is closed the screw moves forward to inject molten plastic into the mould cavity. When the mould is full, cool water running through mould halves, outside the cavity, cools the plastic so it somewhat solidifies. The entire process from the mould closing, injection and opening again takes approximately 3 to 5 seconds.
The moulded "disc" (referred to as a 'green' disc, lacking final processing) is removed from the mould by
vacuumhandling; high-speed robot arms with vacuum suction caps. They are moved onto the finishing line infeed conveyor, or cooling station, in preparation for metallisation. At this point the discs are clear and contain all the digital information desired; however they cannot be played because there is no reflective layer.
The discs pass, one at a time, into the metaliser, a small chamber at approximately 10E-3
Torrvacuum. The process is called ' sputtering'. The metaliser contains a metal "target" -- almost always an alloy of (mostly) aluminium and small amounts of other metals. There is a load-lock system (similar to an airlock) so the process chamber can be kept at high vacuum as the discs are exchanged. When the disc is rotated into the processing position by a swivel arm in the vacuum chamber, a small dose of argon gas is injected into the process chamber and a 700 Volt DC electrical current at up to 20 kWis applied to the target. This produces a plasma from the target, and the plasma vapor is deposited onto the disc; it is an anode - cathode transfer. The metal coats the data side of the disc (upper surface), covering the pit and lands. This metal layer is the reflectivesurface which can be seen on the reverse (non label side) of a CD. This thin layer of metal is subject to corrosion from various contaminants and so is protected by a thin layer of lacquer.
After metalisation, the discs pass on to a spin-coater, where UV curable lacquer is dispensed onto the newly metallized layer. By rapid spinning, the lacquer coats the entire disc with a very thin layer (circa 70 nm). After the lacquer is applied, the disks pass under a high intensity UV lamp which cures the lacquer rapidly. The lacquer also provides a surface for a label, generally screen printed or offest printed. The printing ink(s) must be chemically compatible with the lacquer used. Markers used by consumers to write on blank surfaces are not always, which can lead to breaks in the protective lacquer layer, to corrosion of the reflective layer, and failure of the CD.
quality control, both the stamper and the moulded discs are tested before a production run. Samples of the disc (test pressings) are taken during long production runs and tested for quality consistency. Pressed discs are analyzed on a signal analysis machine. The metal stamper can also be tested on a signal analysis machine which has been specially adapted (larger diameter, more fragile, ...). The machine will "play" the disc or stamper and measure various physical and electrical parameters. Errors can be introduced at every step of production, but the moulding process is the least subject to adjustment. Error sources of errors are more readily identified and compensated for during mastering. If the errors are too severe then the stamper is rejected and a replacement installed. An experienced machine operator can interpret the report from the analysis system and optimise the moulding process to make a disc that meets the required Rainbow Book specification (e.g. Red Book for Audio from the Rainbow Booksseries).
If no defects are found, the CD continues to printing so a
labelcan be screen or offset printed on the top surface of the disc. Thereafter, disks are counted, packaged, and shipped.
[http://www.performanceimpressions.com/Asheville_CD_&_DVD_Printing_&_Duplication.html Pro CD Replication Packages - Performance Impressions - Asheville]
Wikimedia Foundation. 2010.
Look at other dictionaries:
Compact Disc manufacturing — A compact disc in its jewel case. Compact disc manufacturing is the process by which commercial compact discs (CDs) are replicated in mass quantities using a master version created from a source recording. This may be either in audio form (CD… … Wikipedia
Compact Disc — CD redirects here. For other uses, see CD (disambiguation). Not to be confused with DVD. Compact disc The readable surface of a Compact Disc incl … Wikipedia
Compact Disc bronzing — CD affected by bronzing CD bronzing is a specific variant of disc rot, a type of corrosion that affects the reflective layer of CDs and renders them unreadable over time. The phenomenon was first reported by John McKelvey in the September/October … Wikipedia
Compact Disc and DVD copy protection — CD/DVD copy protection is a blanket term for various methods of copy protection for CDs and DVDs. Such methods include DRM, CD checks, Dummy Files, illegal tables of contents, over sizing or over burning the CD, physical errors, and bad sectors.… … Wikipedia
Extended Resolution Compact Disc — (XRCD) is a mastering and manufacture process patented by JVC for producing high fidelity redbook Compact Discs. It was first introduced in 1995.A XRCD is priced about twice as high as a regular full priced CD. JVC attributes this to the higher… … Wikipedia
Disc Makers — Type Private Industry Music, Independent Music, CD Manufacturing, and Manufacturing Founded Philadelphia, Pennsylvania (1966) Founder(s) Ivin Ballen … Wikipedia
Disc rot — is a phrase describing the tendency of CD or DVD or other optical disks to become unreadable due to physical or chemical deterioration. The causes of this effect vary from oxidation of the reflective layer, to physical scuffing and abrasion of… … Wikipedia
Sony Digital Audio Disc Corporation — (Sony DADC) is a manufacturer of Compact Discs, DVDs, UMDs, and Blu ray Discs. The company has many plants worldwide. Although it primarily services Sony owned record labels, it also manufactures discs for other labels. Sony DADC s first plant,… … Wikipedia
WEA Manufacturing — was a Compact Disc manufacturing plant in Olyphant, Pennsylvania that began to manufacture compacts disc in the United States in 1987. Along with Sony s plant, Digital Audio Disc Corporation (DADC) based in Terre Haute, Indiana both plants were… … Wikipedia
Blu-ray Disc — Blue ray redirects here. For the fish of the same name, see Neoraja caerulea. Blu ray Disc Media type … Wikipedia