- Submerged arc welding
Submerged Arc Welding (SAW) is a common
arc weldingprocess. Originally devolved by the Linde - Union Carbide Company. It requires a continuously fed consumable solid or tubular (flux cored) electrode. The molten weld and the arc zone are protected from atmospheric contamination by being “submerged” under a blanket of granular fusible flux consisting of lime, silica, manganese oxide, calcium fluoride, and other compounds. When molten, the flux becomes conductive, and provides a current path between the electrode and the work. This thick layer of flux completely covers the molten metal thus preventing spatter and sparks as well as suppressing the intense ultraviolet radiation and fumes that are a part of the SMAW ( shielded metal arc welding) process.
SAW is normally operated in the automatic or mechanized mode, however, semi-automatic (hand-held) SAW guns with pressurized or gravity flux feed delivery are available. The process is normally limited to the Flat or Horizontal-Fillet welding positions (although Horizontal Groove position welds have been done with a special arrangement to support the flux). Deposition rates approaching 100 lb/h (45 kg/h) have been reported — this compares to ~10 lb/h (5 kg/h) (max) for
shielded metal arc welding. Although Currents ranging from 300 to 2000 A are commonly utilized,Kalpakjian, Serope, and Steven Schmid. Manufacturing Engineering and Technology. '5th ed'. Upper Saddle river, NJ: Pearson Prentice Hall, 2006.] currents of up to 5000 A have also been used (multiple arcs).
Single or multiple (2 to 5) electrode wire variations of the process exist. SAW strip-cladding utilizes a flat strip electrode (e.g. 60 mm wide x 0.5 mm thick). DC or AC power can be utilized, and combinations of DC and AC are common on multiple electrode systems. Constant Voltage welding power supplies are most commonly used, however Constant Current systems in combination with a voltage sensing wire-feeder are available.
SAW filler material usually is a standard wire as well as other special forms. This wire normally has a thickness of 1/16 in. to 1/4 in. (1.6mm to 6mm). In certain circumstances, twisted wire can be used to give the arc an oscillating movement. This helps fuse the toe of the weld to the base metal.Jeffus, Larry. Welding: Principles and Applications. Florence, KY: Thomson Delmar Learning, 2002.]
* Carbon steels (structural and vessel construction);
* Low alloy steels;
* Stainless steels;
* Nickel-based alloys;
* Surfacing applications (wearfacing, build-up, and corrosion resistant overlay of steels).
Advantages of SAW
* High deposition rates (over 100 lb/h (45 kg/h) have been reported);
* High operating factors in mechanized applications;
* Deep weld penetration;
* Sound welds are readily made (with good process design and control);
* High speed welding of thin sheet steels up to 5 m/min (16 ft/min) is possible;
* Minimal welding fume or arc light is emitted.· Practically no edge preparation is necessary· The process is suitable for both indoor and outdoor works.· Distortion is much less.· Welds produced are sound, uniform, ductile, corrosion resistant and have good impact value.· Single pass welds can be made in thick plates with normal equipment.· The arc is always covered under a blanket of flux, thus there is no chance of spatter of weld.
Limitations of SAW
* Limited to ferrous (steel or stainless steels) and some nickel based alloys;
* Normally limited to the 1F, 1G, and 2F positions;
* Normally limited to long straight seams or rotated pipes or vessels;
* Requires relatively troublesome flux handling systems;
* Flux and slag residue can present a health & safety issue;
* Requires inter-pass and post weld slag removal.
Key SAW process variables
* Wire Feed Speed (main factor in welding current control);
* Arc Voltage;
* Travel Speed;
* Electrode Stick-Out (ESO) or Contact Tip to Work (CTTW);
* Polarity and Current Type (AC or DC).
* Flux depth/width;
* Flux and electrode classification and type;
* Electrode wire diameter;
* Multiple electrode configurations.
* [http://www.millerwelds.com/pdf/Submerged.pdf Submerged Arc Welding Pamphlet]
American Welding Society, Welding Handbook, Vol 2 (9th ed.)
Wikimedia Foundation. 2010.
Look at other dictionaries:
Submerged arc welding — Submerged arc welding. См. Дуговая сварка под флюсом. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) … Словарь металлургических терминов
submerged-arc welding — Смотри сварка под флюсом … Энциклопедический словарь по металлургии
Series submerged arc welding — Series submerged arc welding. См. Последовательная дуговая сварка под флюсом. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) … Словарь металлургических терминов
Arc welding — uses a welding power supply to create an electric arc between an electrode and the base material to melt the metals at the welding point. They can use either direct (DC) or alternating (AC) current, and consumable or non consumable electrodes.… … Wikipedia
Gas tungsten arc welding — TIG welding of a bronze sculpture Gas tungsten arc welding (GTAW), also known as tungsten inert gas (TIG … Wikipedia
Gas metal arc welding — RMD redirects here. RMD may also refer to IRA Required Minimum Distributions. Gas metal arc welding … Wikipedia
Shielded metal arc welding — (SMAW), also known as manual metal arc (MMA) welding, flux shielded arc welding … Wikipedia
Welding — is a fabrication process that joins materials, usually metals or thermoplastics, by causing coalescence. This is often done by melting the workpieces and adding a filler material to form a pool of molten material (the weld puddle ) that cools to… … Wikipedia
Welding joints — are formed by welding two or more workpieces, made of metals or plastics, according to a particular geometry. The most common types are butt and lap joints; there are various lesser used welding joints including flange and corner joints. Contents … Wikipedia
welding — Technique for joining metallic parts, usually through the application of heat. Discovered in the 1st millennium AD during attempts to manipulate iron into useful shapes, the technique produced a strong, tough blade. Welding traditionally involved … Universalium