Glass beadmaking


Glass beadmaking

The technology for glass beadmaking is among the oldest human arts, dating back 30,000 years (Dubin, 1987). Glass beads have been dated back to at least Roman times. Perhaps the earliest glass-like beads were Egyptian faience beads, a form of clay bead with a self-forming vitreous coating.

Common types of glass bead manufacture

Glass beads are usually categorized by the method used to manipulate the glass. Most beads fall into three main categories: wound beads, drawn beads, and molded beads. There are composites, such as millefiori beads, where cross-sections of a drawn glass cane are applied to a wound glass core. A very minor industry in blown glass beads also existed in 19th century Venice and France.

Wound glass beads

Probably the earliest beads of true glass were made by the winding method. Glass at a temperature high enough to make it workable, or "ductile", is laid down or wound around a steel wire or mandrel coated in a clay slip called "bead release." The wound bead, while still hot, may be further shaped by manipulating with graphite, wood, stainless steel or marble tools and paddles. This process is called marvering, originating from the French word "marver" which translates to "marble". It can also be pressed into a mold in its molten state. While still hot, or after re-heating, the surface of the bead may be decorated with fine rods called stringers of colored glass. These are a type of lampwork beads.

Drawn glass beads

The drawing of glass is also very ancient. Evidence of large-scale drawn-glass beadmaking has been found by archeologists in India, at sites like Arekamedu dating to the 2nd century CE. The small drawn beads made by that industry have been called Indo-Pacific beads, because they may have been the single most widely traded item in history--found from the islands of the Pacific to Great Zimbabwe in southern Africa. There are several methods for making drawn beads, but they all involve pulling a strand out of a gather of glass in such a way as to incorporate a bubble in the center of the strand to serve as the hole in the bead. In Arekamedu this was accomplished by inserting a hollow metal tube into the ball of hot glass and pulling the glass strand out around it, to form a continuous glass tube. In the Venetian bead industry, molten glass was gathered on the end of a tool called a puntile ("puntying up"), a bubble was incorporated into the center of a gather of molten glass, and a second puntile was attached before stretching the gather with its internal bubble into a long cane. The pulling was a skilled process, and canes were reportedly drawn to lengths up to convert|200|ft|m long. The drawn tube was then chopped, producing individual drawn beads from its slices. The resulting beads were cooked or rolled in hot sand to round the edges without melting the holes closed; were sieved into sizes; and, usually, strung onto hanks for sale.

The most common type of modern glass bead is the seed bead, a small type of bead typically less than 6 mm, traditionally monochrome, and manufactured in very large quantities.They are a modern example of mechanically-drawn glass beads. The micro-bead or "seed bead", are so called due to their tiny, regular size. Modern seed beads are extruded by machine and some, such as Miyuki delicas, look like small tubes.

Molded beads

Pressed or molded beads are associated with higher labour costs. These are made in the Czech republic, in what was once called Bohemia. Thick rods are heated to molten and fed into a complex apparatus that stamps the glass, including a needle that pierces a hole. The beads again are rolled in hot sand to remove flashing and soften seam lines. By making canes (the glass rods fed into the machine) striped or otherwise patterned, the resulting beads can be more elaborately colored than seed beads. One `feed' of a hot rod might result in 10-20 beads, and a single operator can make thousands in a day.

The Bohemian glass industry was known for its ability to copy more expensive beads, and produced molded glass "lion's teeth", "coral", and "shells", which were popular in the 19th and early 20th century Africa trade.

Lampwork beads

A variant of the wound glass beadmaking technique, and a labor intensive one, is what is traditionally called lampworking. In the Venetian industry, where very large quantities of beads were produced in the 19th century for the African trade, the core of a decorated bead was produced from molten glass at furnace temperatures, a large-scale industrial process dominated by men. The delicate multicolored decoration was then added by people, mostly women, working at home using an oil lamp or spirit lamp to re-heat the cores and the fine wisps of colored glass used to decorate them. These workers were paid on a piecework basis for the resulting lampwork beads. Modern lampwork beads are made by using a gas torch to heat a rod of glass and spinning the resulting thread around a metal rod covered in bead release. When the base bead has been formed, other colors of glass can be added to the surface to create many designs. After this initial stage of the beadmaking process, the bead can be further fired in a kiln to make it more durable.

Modern beadmakers use single or dual fuel torches, so `flameworked' is replacing the older term. Unlike a metalworking torch, or burner as some people in the trade prefer to call them, a flameworking torch is usually "surface mix"; that is, the oxygen and fuel (typically propane, though natural gas is also common) is mixed after it comes out of the torch, resulting in a quieter tool and less dirty flame. Also unlike metalworking, the torch is fixed, and the bead and glass move in the flame. American torches are usually mounted at about a 45 degree angle, a result of scientific glassblowing heritage; Japanese torches are recessed, and have flames coming straight up, like a large bunsen burner; Czech production torches tend to be positioned nearly horizontally.

Dichroic glass beads

Increasingly, dichroic glass is being used to produce high-end art beads. Dichroic glass has a thin film of metal fused to the surface of the glass, resulting in a surface that has a metallic sheen that changes between two colors when viewed at different angles. Beads can be pressed, or made with traditional lampworking techniques. If the glass is kept in the flame too long, the metallic coating will turn silver and burn off.

Furnace glass

Italian glass blowing techniques such as latticinio and zanfirico are adapted here to make beads. Furnace glass uses large decorated canes built up out of smaller canes, encased in clear glass and then extruded to form the beads with linear and twisting stripe patterns. No air is blown into the glass. These beads require a large scale glass furnace and annealing kiln for manufacture.

Lead crystal

Lead crystal beads are machine cut and polished. Their high lead content makes them sparkle more than other glass, but also makes them inherently fragile.

Other methods for making glass beads

Lead glass (for neon signs) and, especially borosilicate is available in tubing, making true blown beads possible. (Soda-lime glass can be blown at the end of a metal tube, or, more commonly wound on the mandrel to make a hollow bead, but the former is unusual and the latter not a true mouth-blown technique.) In addition, beads can be fused from sheet glass or using ground glass.

Modern Ghana has a lively industry in beads molded from powdered glass. Also in Africa, the famed Kiffa beads are made in Mauritania, historically by women, using powdered glass that the beadmaker usually grinds herself from commercially available glass seed beads and recycled glass.

Molded ground glass, if painted into the mold, is called pate de verre, and the technique can be used to make beads, though pendants and cabochons are more typical. Lampwork (and other) beads can be painted with glass paints.

ee also

* Murano beads
* Glass art
*

External links

* [http://www.locallygrownart.com/ Glassblowing Resources and Education]
* [http://www.evileyebead.com/ Authentic glass evil eye bead making in Anatolia]


Wikimedia Foundation. 2010.

Look at other dictionaries:

  • Glass art — and Glass sculpture is the use of glass as an artistic medium to produce sculptures or two dimensional artworks. Specific approaches include stained glass, working glass in a torch flame (lampworking), glass beadmaking, glass casting, glass… …   Wikipedia

  • Glass — This article is about the material. For other uses, see Glass (disambiguation). Moldavite, a natural glass formed by meteorite impact, from Besednice, Bohemia …   Wikipedia

  • Glass recycling — Public glass waste collection point in a neighborhood area for separating colorless, green and amber glass …   Wikipedia

  • Studio glass — Glass ball made by Tyler Hopkins. Glass can be made transparent and flat, or into other shapes and colors as shown in this sphere from the Verrerie of Brehat in Brittany …   Wikipedia

  • Stained glass — For the Blackford Oakes novel, see Stained Glass (novel) The term stained glass refers either to the material of coloured glass or to the art and craft of working with it. Throughout its thousand year history the term stained glass was applied… …   Wikipedia

  • Crown glass (window) — This article is about the window glass. For the optical glass, see Crown glass (optics). Crown Glass Crown glass was an early type of window glass. In this process, glass was blown into a crown or hollow globe. This was then transferred from the… …   Wikipedia

  • Powder glass beads — The earliest powder glass beads on record were discovered during archaeological excavations at Mapungubwe, in present day Zimbabwe, and dated to 970 1000 CE. In our time, the main area of powder glass bead manufacture is West Africa, most… …   Wikipedia

  • Cylinder blown sheet glass — Cylinder blown sheet is a type of hand blown window glass. It is created with a similar process to broad sheet, but larger cylinders are produced by swinging the cylinder in a trench. The glass is then allowed to cool before the cylinder is cut.… …   Wikipedia

  • Moss agate glass — Detail from a Moss Agate vase by John Northwood, c.1888 Moss Agate glass is a type of art glass developed in 1888 at the noted glasshouse Stevens Williams by glassmaker John Northwood, with the assistance of Will Bridges, then manager of the firm …   Wikipedia

  • Bead — For other uses, see Bead (disambiguation). Beads A bead is a small, decorative object that is usually pierced for threading or stringing. Beads range in size from under 1 millimetre (0.039 in) to over 1 centimetre (0.39 in) in diameter …   Wikipedia


Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”

We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.