Electroless nickel plating, or "EN", is an electroplating technique used to deposit a layer of nickel- phosphorous alloy on a solid work piece, such as metals or plastic. The alloys with different percentage of phosphorus, ranging from 2-5 (low phosphorus) to up to 11-14 (high phosphorus) are possible. The metallurgical properties of alloys depend on the percentage of phosphorus.

Overview

Electroless nickel plating is an auto-catalytic reaction used to deposit a coating of nickel on a substrate. Unlike electroplating, it is not necessary to pass an electric current through the solution to form a deposit. This plating technique is to prevent corrosion and wear. EN techniques can also be used to manufacture composite coatings by suspending powder in the bath.

Electroless nickel plating has several advantages versus electroplating. Free from flux-density and power supply issues, it provides an even deposit regardless of workpiece geometry, and with the proper pre-plate catalyst, can deposit on non-conductive surfaces.

Pretreatment of parts for EN plating

Before performing electroless nickel plating, the material to be plated must be cleaned by a series of cleaning chemicals such as bases and acids, this process is called the pre-treatment process. Failure to remove unwanted "soils" from the part's surface would result in poor plating. Each pre-treatment chemical must be followed by water rinsing (normally two to three times) to remove the chemical that adheres to the surface. Degreasing removes oils from surface; acid cleaning removes scaling. Activation is done with a weak acid etch, or nickel strike, or, in the case of non-metallic substrate, a proprietary solution. After the plating process, plated materials must be finished with an anti-oxidation or anti-tarnish chemical (trisodium phosphate, chromate etc) and pure water rinsing to prevent unwanted stains. The rinsing materials must then be completely dried off or sometimes baked off to obtain the full hardness of the plating film.

Advantages of EN

# Does not use electrical power.
# Even coating on parts surface can be achieved.
# No sophisticated jigs or racks are required.
# There is flexibility in plating volume and thickness.
# The process can plate recesses and blind holes with stable thickness.
# Chemical replenishment can be monitored automatically.
# Complex filtration method is not required
# Matte, Semi Bright or Bright finishes can be obtained.

Each type of electroless nickel also has particular advantages depending on the application and type of nickel alloy.Fact sheet on Electroless Nickel from Erie Plating Company website, http://erieplating.com/electroless-nickel . Used with their permission.]

Medium phosphorus electroless nickel

# Very bright and semi-bright options
# High speed deposit rate
# Very stable
# The most common type of electroless nickel applied

High phosphorus electroless nickel

# Superior corrosion protection
# Lower porosity
# Non-magnetic
# Less prone to staining
# Pit-free deposits

Disadvantages of EN

# Lifespan of chemicals is limited.
# Waste treatment cost is high due to the speedy chemical renewal.

Applications

The most common form of Electroless nickel plating produces a nickel phosphorus alloy coating. The phosphorus content in electroless nickel coatings can range from 2% to 13% It is commonly used in engineering coating applications where wear resistance, hardness and corrosion protection are required. Applications include oil field valves, rotors, drive shafts, paper handling equipment, fuel rails, optical surfaces for diamond turning, door knobs, kitchen utensils, bathroom fixtures, electrical/mechanical tools and office equipment. It is also commonly used as a coating in electronics printed circuit board manufacturing, typically with an overlay of gold to prevent corrosion. This process is known by the acronym ENIG, which stands for "Electroless Nickel, Immersion Gold".

Due to the high hardness of the coating it can be used to salvage worn parts. Coatings of 1-4 mils can be applied and machined back to final dimensions. Its uniform deposition profile mean it can be applied to complex components not readily suited to other hard wearing coatings like hard chromium.

It is also used extensively in the manufacture of hard disk drives, as a magnetically neutral base coating on aluminium platters (disks) prior to finishing with an magnetic read/write iron oxide coating.Its use in the automotive industry for wear resistance has increased significantly, however it is important to recognise that only EOLVD or RoHS compliant process types (free from heavy metal stabilizers) may be used for these applications.

pecifications

*AMS-2404
*AMS-C-26074
*ASTM B-733
*ASTM-B-656
*MIL-DTL-32119

ee also

*Electroplating

References


Wikimedia Foundation. 2010.

Look at other dictionaries:

  • Nickel plating — may refer to: Nickel electroplating Electroless nickel plating This disambiguation page lists articles associated with the same title. If an internal link led you here, you may wish to change the li …   Wikipedia

  • Plating — describes surface covering where a metal is deposited on a conductive surface. Plating has been done for hundreds of years, but it is also critical for modern technology. Plating is used to decorate objects, for corrosion inhibition, to improve… …   Wikipedia

  • Nickel electroplating — is a technique of electroplating a thin layer of nickel onto a metal object. The nickel layer can be decorative, provide corrosion resistance, wear resistance, or used to build up worn or undersized parts for salvage purposes.[1] Contents 1… …   Wikipedia

  • electroless — [ɪ lɛktrəʊlɪs] adjective denoting nickel plating using chemical rather than electrical means …   English new terms dictionary

  • electroless plating — /i lek troh lis/ a technique of plating metal by chemical rather than electrical means, in which the piece to be plated is immersed in a reducing agent that, when catalyzed by certain materials, changes metal ions to metal that forms a deposit on …   Universalium

  • plating — /play ting/, n. 1. a thin coating of gold, silver, etc. 2. an external layer of metal plates. 3. the act of a person or thing that plates. [1535 45; PLATE1 + ING1] * * * Coating a metal or other material, such as plastic or china, with a hard,… …   Universalium

  • Gold plating — is a method of depositing a thin layer of gold onto the surface of another metal, most often copper or silver, by chemical or electrochemical means.Mechanical or chemical affixing of thin gold foils onto the surface of objects is instead known as …   Wikipedia

  • Coventya — Type limited company Industry Chemical Industry Founded 1927 then known as Société Continentale Parker …   Wikipedia

  • Electroplating — is the process of using electrical current to reduce cations of a desired material from a solution and coat a conductive object with a thin layer of the material, such as a metal. Electroplating is primarily used for depositing a layer of… …   Wikipedia

  • Zincate — Not to be confused with zincite. In chemistry the term zincate may refer to a salt containing Zn(OH)42−,also called the tetrahydroxozincate ion. It is an ore of Zinc. Examples include calcium zincate CaZn(OH)4.2H2O [1] or Na2Zn(OH)4[2] or the… …   Wikipedia


Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”

We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.