Nylon


Nylon
Nylon Nylon Nylon 6,6 unit
Density 1.15 g/cm3
Electrical conductivity (σ) 10−12 S/m
Thermal conductivity 0.25 W/(m·K)
Melting point 463–624 K
190–350 °C
374–663 °F

Nylon is a generic designation for a family of synthetic polymers known generically as polyamides, first produced on February 28, 1935, by Wallace Carothers at DuPont's research facility at the DuPont Experimental Station. Nylon is one of the most commonly used polymers.

Contents

Overview

Nylon is a thermoplastic, silky material, first used commercially in a nylon-bristled toothbrush (1938), followed more famously by women's stockings ("nylons"; 1940). It is made of repeating units linked by amide bonds and is frequently referred to as polyamide (PA). Nylon was the first commercially successful synthetic polymer. There are two common methods of making nylon for fiber applications. In one approach, molecules with an acid (-COOH) group on each end are reacted with molecules containing amine (-NH2) groups on each end. The resulting nylon is named on the basis of the number of carbon atoms separating the two acid groups and the two amines. These are formed into monomers of intermediate molecular weight, which are then reacted to form long polymer chains.

Nylon was intended to be a synthetic replacement for silk and substituted for it in many different products after silk became scarce during World War II. It replaced silk in military applications such as parachutes and flak vests, and was used in many types of vehicle tires.

Nylon fibres are used in many applications, including fabrics, bridal veils, carpets, musical strings, and rope.

Solid nylon is used for mechanical parts such as machine screws, gears and other low- to medium-stress components previously cast in metal. Engineering-grade nylon is processed by extrusion, casting, and injection molding. Solid nylon is used in hair combs. Type 6,6 Nylon 101 is the most common commercial grade of nylon, and Nylon 6 is the most common commercial grade of molded nylon. For use in tools such as the Apple Black Stick, a nylon is available in glass-filled variants which increase structural and impact strength and rigidity, and molybdenum sulfide-filled variants which increase lubricity.

Aramids are another type of polyamide with quite different chain structures which include aromatic groups in the main chain. Such polymers make excellent ballistic fibres.

Chemistry

Nylons are condensation copolymers formed by reacting equal parts of a diamine and a dicarboxylic acid, so that amides are formed at both ends of each monomer in a process analogous to polypeptide biopolymers. Chemical elements included are carbon, hydrogen, nitrogen, and oxygen. The numerical suffix specifies the numbers of carbons donated by the monomers; the diamine first and the diacid second. The most common variant is nylon 6-6 which refers to the fact that the diamine (hexamethylene diamine, IUPAC name: hexane-1,6-diamine) and the diacid (adipic acid, IUPAC name: hexanedioic acid) each donate 6 carbons to the polymer chain. As with other regular copolymers like polyesters and polyurethanes, the "repeating unit" consists of one of each monomer, so that they alternate in the chain. Since each monomer in this copolymer has the same reactive group on both ends, the direction of the amide bond reverses between each monomer, unlike natural polyamide proteins which have overall directionality: C terminal → N terminal. In the laboratory, nylon 6-6 can also be made using adipoyl chloride instead of adipic.

It is difficult to get the proportions exactly correct, and deviations can lead to chain termination at molecular weights less than a desirable 10,000 daltons (u). To overcome this problem, a crystalline, solid "nylon salt" can be formed at room temperature, using an exact 1:1 ratio of the acid and the base to neutralize each other. Heated to 285 °C (545 °F), the salt reacts to form nylon polymer. Above 20,000 daltons, it is impossible to spin the chains into yarn, so to combat this, some acetic acid is added to react with a free amine end group during polymer elongation to limit the molecular weight. In practice, and especially for 6,6, the monomers are often combined in a water solution. The water used to make the solution is evaporated under controlled conditions, and the increasing concentration of "salt" is polymerized to the final molecular weight.

DuPont patented[1] nylon 6,6, so in order to compete, other companies (particularly the German BASF) developed the homopolymer nylon 6, or polycaprolactam — not a condensation polymer, but formed by a ring-opening polymerization (alternatively made by polymerizing aminocaproic acid). The peptide bond within the caprolactam is broken with the exposed active groups on each side being incorporated into two new bonds as the monomer becomes part of the polymer backbone. In this case, all amide bonds lie in the same direction, but the properties of nylon 6 are sometimes indistinguishable from those of nylon 6,6 — except for melt temperature and some fiber properties in products like carpets and textiles. There is also nylon 9.

The 428 °F (220 °C) melting point of nylon 6 is lower than the 509 °F (265 °C) melting point of nylon 6,6.[2]

Nylon 5,10, made from pentamethylene diamine and sebacic acid, was studied by Carothers even before nylon 6,6 and has superior properties, but is more expensive to make. In keeping with this naming convention, "nylon 6,12" (N-6,12) or "PA-6,12" is a copolymer of a 6C diamine and a 12C diacid. Similarly for N-5,10 N-6,11; N-10,12, etc. Other nylons include copolymerized dicarboxylic acid/diamine products that are not based upon the monomers listed above. For example, some aromatic nylons are polymerized with the addition of diacids like terephthalic acid (→ Kevlar, Twaron) or isophthalic acid (→ Nomex), more commonly associated with polyesters. There are copolymers of N-6,6/N6; copolymers of N-6,6/N-6/N-12; and others. Because of the way polyamides are formed, nylon would seem to be limited to unbranched, straight chains. But "star" branched nylon can be produced by the condensation of dicarboxylic acids with polyamines having three or more amino groups.

The general reaction is:

Condensation polymerization diacid diamine.svg

A molecule of water is given off and the nylon is formed. Its properties are determined by the R and R' groups in the monomers. In nylon 6,6, R = 4C and R' = 6C alkanes, but one also has to include the two carboxyl carbons in the diacid to get the number it donates to the chain. In Kevlar, both R and R' are benzene rings.

Concepts of nylon production

The first approach: combining molecules with an acid (COOH) group on each end are reacted with two chemicals that contain amine (NH2) groups on each end. This process creates nylon 6,6, made of hexamethylene diamine with six carbon atoms and adipic acid.

The second approach: a compound has an acid at one end and an amine at the other and is polymerized to form a chain with repeating units of (-NH-[CH2]n-CO-)x. In other words, nylon 6 is made from a single six-carbon substance called caprolactam. In this equation, if n = 5, then nylon 6 is the assigned name (may also be referred to as polymer).

The characteristic features of nylon 6,6 include:

  • Pleats and creases can be heat-set at higher temperatures
  • More compact molecular structure
  • Better weathering properties; better sunlight resistance
  • Softer "Hand"
  • Higher melting point (256 °C/492.8 °F)
  • Superior colorfastness
  • Excellent abrasion resistance

On the other hand, nylon 6 is easy to dye, more readily fades; it has a higher impact resistance, a more rapid moisture absorption, greater elasticity and elastic recovery.

Characteristics

  • Variation of luster: nylon has the ability to be very lustrous, semilustrous or dull.
  • Durability: its high tenacity fibers are used for seatbelts, tire cords, ballistic cloth and other uses.
  • High elongation
  • Excellent abrasion resistance
  • Highly resilient (nylon fabrics are heat-set)
  • Paved the way for easy-care garments
  • High resistance to insects, fungi, animals, as well as molds, mildew, rot and many chemicals
  • Used in carpets and nylon stockings
  • Melts instead of burning
  • Used in many military applications
  • Good specific strength
  • Transparent to infrared light (−12dB)[3]

Bulk properties

Above their melting temperatures, Tm, thermoplastics like nylon are amorphous solids or viscous fluids in which the chains approximate random coils. Below Tm, amorphous regions alternate with regions which are lamellar crystals.[4] The amorphous regions contribute elasticity and the crystalline regions contribute strength and rigidity. The planar amide (-CO-NH-) groups are very polar, so nylon forms multiple hydrogen bonds among adjacent strands. Because the nylon backbone is so regular and symmetrical, especially if all the amide bonds are in the trans configuration, nylons often have high crystallinity and make excellent fibers. The amount of crystallinity depends on the details of formation, as well as on the kind of nylon. Apparently it can never be quenched from a melt as a completely amorphous solid.

Nylon 6,6 can have multiple parallel strands aligned with their neighboring peptide bonds at coordinated separations of exactly 6 and 4 carbons for considerable lengths, so the carbonyl oxygens and amide hydrogens can line up to form interchain hydrogen bonds repeatedly, without interruption. Nylon 5,10 can have coordinated runs of 5 and 8 carbons. Thus parallel (but not antiparallel) strands can participate in extended, unbroken, multi-chain β-pleated sheets, a strong and tough supermolecular structure similar to that found in natural silk fibroin and the β-keratins in feathers. (Proteins have only an amino acid α-carbon separating sequential -CO-NH- groups.) Nylon 6 will form uninterrupted H-bonded sheets with mixed directionalities, but the β-sheet wrinkling is somewhat different. The three-dimensional disposition of each alkane hydrocarbon chain[disambiguation needed ] depends on rotations about the 109.47° tetrahedral bonds of singly bonded carbon atoms.

When extruded into fibers through pores in an industrial spinneret, the individual polymer chains tend to align because of viscous flow. If subjected to cold drawing afterwards, the fibers align further, increasing their crystallinity, and the material acquires additional tensile strength.[5] In practice, nylon fibers are most often drawn using heated rolls at high speeds.

Block nylon tends to be less crystalline, except near the surfaces due to shearing stresses during formation. Nylon is clear and colorless, or milky, but is easily dyed. Multistranded nylon cord and rope is slippery and tends to unravel. The ends can be melted and fused with a heat source such as a flame or electrode to prevent this.

When dry, polyamide is a good electrical insulator. However, polyamide is hygroscopic. The absorption of water will change some of the material's properties such as its electrical resistance. Nylon is less absorbent than wool or cotton.

Historical uses

Bill Pittendreigh, DuPont, and other individuals and corporations worked diligently during the first few months of World War II to find a way to replace Asian silk and hemp with nylon in parachutes. It was also used to make tires, tents, ropes, ponchos, and other military supplies. It was even used in the production of a high-grade paper for U.S. currency. At the outset of the war, cotton accounted for more than 80% of all fibers used and manufactured, and wool fibers accounted for nearly all of the rest. By August 1945, manufactured fibers had taken a market share of 25%, at the expense of cotton.

Some of the terpolymers based upon nylon are used every day in packaging. Nylon has been used for meat wrappings and sausage sheaths.

Use in composites

Nylon can be used as the matrix material in composite materials, with reinforcing fibers like glass or carbon fiber; such a composite has a higher density than pure nylon. Such thermoplastic composites (25% glass fiber) are frequently used in car components next to the engine, such as intake manifolds, where the good heat resistance of such materials makes them feasible competitors to metals.

Hydrolysis and degradation

All nylons are susceptible to hydrolysis, especially by strong acids, a reaction essentially the reverse of the synthetic reaction shown above. The molecular weight of nylon products so attacked drops fast, and cracks form quickly at the affected zones. Lower members of the nylons (such as nylon 6) are affected more than higher members such as nylon 12. This means that nylon parts cannot be used in contact with sulfuric acid for example, such as the electrolyte used in lead-acid batteries. When being molded, nylon must be dried to prevent hydrolysis in the molding machine barrel since water at high temperatures can also degrade the polymer. The reaction is of the type:

Amide hydrolysis.png

Incineration and recycling

Various nylons break down in fire and form hazardous smoke, and toxic fumes or ash, typically containing hydrogen cyanide. Incinerating nylons to recover the high energy used to create them is usually expensive, so most nylons reach the garbage dumps, decaying very slowly.[6] Some recycling is done on nylon, usually creating pellets for reuse in the industry.[7]

Etymology

In 1940, John W. Eckelberry of DuPont stated that the letters "nyl" were arbitrary and the "on" was copied from the suffixes of other fibers such as cotton and rayon. A later publication by DuPont explained that the name was originally intended to be "No-Run" ("run" meaning "unravel"), but was modified to avoid making such an unjustified claim and to make the word sound better.[8] An apocryphal explanation is that Nylon is a conflation of "New York" and "London". A humorous backronym is "Now You've Lost, Old Nippon" referring to the supposed loss of demand for Japanese silk.

See also

References

  1. ^ History of Nylon US Patent 2,130,523 'Linear polyamides suitable for spinning into strong pliable fibers', U.S. Patent 2,130,947 'Diamine dicarboxylic acid salt' and U.S. Patent 2,130,948 'Synthetic fibers', all issued September 20, 1938
  2. ^ Typical physical characteristics of nylon at "Basics of Design Engineering"
  3. ^ Bjarnason, J. E.; Chan, T. L. J.; Lee, A. W. M.; Celis, M. A.; Brown, E. R. (2004). "Millimeter-wave, terahertz, and mid-infrared transmission through common clothing". Applied Physics Letters 85 (4): 519. doi:10.1063/1.1771814. 
  4. ^ Valerie Menzer's Nylon 66 Webpage. Arizona University
  5. ^ Nylon | Chemical Heritage Foundation. Chemheritage.org (2011-08-23). Retrieved on 2011-10-17.
  6. ^ Typically 80 to 100% is sent to landfill or garbage dumps, while less than 18% are incinerated while recovering the energy. See Francesco La Mantia (August 2002). Handbook of plastics recycling. iSmithers Rapra Publishing. pp. 19–. ISBN 978-1-85957-325-9. http://books.google.com/books?id=TBrOGJqvgcMC&pg=PA19. Retrieved 17 October 2011. 
  7. ^ Typically 1% or less of nylons are recycled this way.
  8. ^ Context, vol. 7, no. 2, 1978

Further reading

External links

For historical perspectives on nylon, see the Documents List of "The Stocking Story: You Be The Historian" at the Smithsonian website, by The Lemelson Center for the Study of Invention and Innovation, National Museum of American History, Smithsonian Institution.


Wikimedia Foundation. 2010.

Look at other dictionaries:

  • nylon — nylon …   Dictionnaire des rimes

  • nylon — [ nilɔ̃ ] n. m. • 1942; nom déposé, mot angl. amér., p. ê. de (vi)nyl et (cott)on, (ray)on « rayonne » ♦ Fibre synthétique (polyamide), obtenue au moyen de réactions sur des sous produits du goudron. Résistance, élasticité du nylon. Brosse en… …   Encyclopédie Universelle

  • nylon — ylon n. 1. Any of several thermoplastic polyamide plastics, comprising a family of high strength resilient synthetic materials, used mostly in fibers. [WordNet 1.5] 2. A synthetic fabric consisting of fibers of nylon[wn1]. [WordNet 1.5] 3. pl.… …   The Collaborative International Dictionary of English

  • Nylon — steht für: Nylon (Band), eine Berliner Band Nylon, ein Handelsname für Kunstfasern aus Polyamid Diese Seite ist eine Begriffsklärung zur Unterscheidung mehrerer mit demselben Wort bezeichneter Begriffe …   Deutsch Wikipedia

  • nylon — ☆ nylon [nī′län΄ ] n. [arbitrary coinage, infl. by (COTT)ON and (RAY)ON] 1. any of a group of synthetic long chain polymeric amides with recurring amide groups, made into fiber, yarn, bristles, sheets, molded plastics, etc. that have great… …   English World dictionary

  • nylon — nylon, ⊕ nylón → nailon …   Diccionario panhispánico de dudas

  • nylón — nylon, ⊕ nylón → nailon …   Diccionario panhispánico de dudas

  • nylon — (n.) 1938, coined, according to DuPont, from random generic syllable nyl + on, common ending in fiber names (Cf. rayon), said to be ultimately from cotton. Use (in plural) for nylon stockings is from 1940 …   Etymology dictionary

  • Nylon — Nylon: Der Name der Chemiefaser wurde im 20. Jh. aus gleichbed. engl. amerik. nylon, einem Kunstwort ohne sichere Deutung, entlehnt …   Das Herkunftswörterbuch

  • nylon — {{/stl 13}}{{stl 8}}rz. mnż I, D. u, Mc. nylonnie {{/stl 8}}{{stl 20}} {{/stl 20}}{{stl 12}}1. {{/stl 12}}{{stl 7}} włókno syntetyczne cechujące się wytrzymałością, elastycznością, odpornością na gniecenie 2. tkanina, materiał wykonany z tego… …   Langenscheidt Polski wyjaśnień

  • nylon — ► NOUN 1) a tough, lightweight, elastic synthetic polymer with a protein like chemical structure. 2) fabric or yarn made of such polymers. 3) (nylons) nylon stockings or tights. ORIGIN an invented word …   English terms dictionary


Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”

We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.