Polylactic acid


Polylactic acid
The skeletal formula of poly(lactic acid)

Poly(lactic acid) or polylactide (PLA) is a thermoplastic aliphatic polyester derived from renewable resources, such as corn starch (in the United States), tapioca products (roots, chips or starch mostly in Asia) or sugarcanes (in the rest of world). It can biodegrade under certain conditions, such as the presence of oxygen, and is difficult to recycle.

The name "polylactic acid" is to be used with caution, not complying to standard nomenclatures (such as IUPAC) and potentially leading to ambiguity (PLA is not a polyacid (polyelectrolyte), but rather a polyester)[citation needed].

Contents

Synthesis

Catalytic and thermolytic ring-opening polymerization of lactide (left) to polylactide (right)

Bacterial fermentation is used to produce lactic acid from corn starch or cane sugar. However, lactic acid cannot be directly polymerized to a useful product, because each polymerization reaction generates one molecule of water, the presence of which degrades the forming polymer chain to the point that only very low molecular weights are observed. Instead, two lactic acid molecules undergo a single esterfication and then catalytically cyclized to make a cyclic dilactate ester. Although dimerization also generates water, it can be separated prior to polymerization due to a significant drop in polarity. PLA of high molecular weight is produced from the dilactate ester by ring-opening polymerization using most commonly a stannous octoate[citation needed] catalyst, but for laboratory demonstrations tin(II) chloride is often employed. This mechanism does not generate additional water, and hence, a wide range of molecular weights is accessible.

Polymerization of a racemic mixture of L- and D-lactides usually leads to the synthesis of poly-DL-lactide (PDLLA) which is amorphous. Use of stereospecific catalysts can lead to heterotactic PLA which has been found to show crystallinity. The degree of crystallinity, and hence many important properties, is largely controlled by the ratio of D to L enantiomers used, and to a lesser extent on the type of catalyst used.

Chemical and physical properties

Due to the chiral nature of lactic acid, several distinct forms of polylactide exist: poly-L-lactide (PLLA) is the product resulting from polymerization of L,L-lactide (also known as L-lactide). PLLA has a crystallinity of around 37%, a glass transition temperature between 60-65 °C, a melting temperature between 173-178 °C and a tensile modulus between 2.7-16 GPa.[1][2] However, heat resistant PLA can withstand temperatures of 110C (230F).[3]

PLA has similar mechanical properties to PETE polymer, but has a significantly lower maximum continuous use temperature.[4]

Polylactic acid can be processed like most thermoplastics into fiber (for example using conventional melt spinning processes) and film. The melting temperature of PLLA can be increased 40-50 °C and its heat deflection temperature can be increased from approximately 60°C to up to 190 °C by physically blending the polymer with PDLA (poly-D-lactide). PDLA and PLLA form a highly regular stereocomplex with increased crystallinity. The temperature stability is maximised when a 50:50 blend is used, but even at lower concentrations of 3-10% of PDLA, there is still a substantial improvement. In the latter case, PDLA acts as a nucleating agent, thereby increasing the crystallization rate. Biodegradation of PDLA is slower than for PLA due to the higher crystallinity of PDLA. PDLA has the useful property of being optically transparent.

There is also poly(L-lactide-co-D,L-lactide) (PLDLLA) – used as PLDLLA/TCP scaffolds for bone engineering[5].

Applications

Mulch film made of polylactic acid (PLA)-blend bio-flex
Biodegradable plastic cups in use at an eatery
Tea bags made of polylactide (PLA). Peppermint tea is enclosed.
Due to PLA's relatively low glass transition temperature, PLA cups cannot hold hot liquids. However, much research is devoted to developing a heat resistant PLA. [6]

Stereocomplex blends of PDLA and PLLA have a wide range of applications, such as woven shirts (ironability), microwavable trays, hot-fill applications and even engineering plastics (in this case, the stereocomplex is blended with a rubber-like polymer such as ABS). Such blends also have good form-stability and visual transparency, making them useful for low-end packaging applications. Progress in biotechnology has resulted in the development of commercial production of the D enantiomer form, something that was not possible until recently.[7]

PLA is currently used in a number of biomedical applications, such as sutures, stents, dialysis media and drug delivery devices. The total degradation time of PLA is a few years.[8] It is also being evaluated as a material for tissue engineering.

Because it is biodegradable, it can also be employed in the preparation of bioplastic, useful for producing loose-fill packaging, compost bags, food packaging, and disposable tableware. In the form of fibers and non-woven textiles, PLA also has many potential uses, for example as upholstery, disposable garments, awnings, feminine hygiene products, and diapers.

PLA has been used as the hydrophobic block of amphiphilic synthetic block copolymers used to form the vesicle membrane of polymersomes.

PLA is a sustainable alternative to petrochemical-derived products, since the lactides from which it is ultimately produced can be derived from the fermentation of agricultural by-products such as corn starch[9] or other carbohydrate-rich substances like maize, sugar or wheat. PLA can be an alternative to high-impact polystyrene by using as much as 1 wt% non-PLA due to creating co-polymers which can strengthen PLA plastic [10].

PLA is more expensive than many petroleum-derived commodity plastics, but its price has been falling as production increases. The demand for corn is growing, both due to the use of corn for bioethanol and for corn-dependent commodities, including PLA.

PLA has also been developed in the United Kingdom to serve as sandwich packaging.[11]

PLA has also been used in France to serve as the binder in Isonat Nat’isol, a hemp fiber building insulation.

PLA is used for biodegradable and compostable disposable cups for cold beverages, the lining in cups for hot beverages, deli containers and clamshells for food packaging.[12] Researchers have improved the glass transition temperature of PLA to use with hot liquids up to 110C (230F). [13]

PLA is being used as a replacement for nylon in "silken" teabags. [14]

The pharmaceutical industry uses oligolactic acid (OLA), a shorter polymer of lactic acid, in pressurized metered dose inhalers (pMDIs) as a surfactant. Studies have shown that on standing, pMDIs without OLA will yield a much higher dose than intended as compared to those containing OLA which delivers a fairly constant dosage.[15]

PLA is used as a feedstock material in 3D printers such as Reprap[16] and Makerbot.[17]

Production

As of Jun 2010, NatureWorks was the primary producer of PLA (bioplastic) in the United States.

Other companies involved in PLA manufacturing are PURAC Biomaterials (The Netherlands) and several Chinese manufacturers. The primary producer of PDLLA is PURAC, a wholly owned subsidiary of [CSM] located in the Netherlands.

Galactic and Total Petrochemicals operate a joint-venture, Futerro, that is developing a second generation of polylactic acid product. This project includes the building of a PLA pilot plant of 1500 tonnes/year in Belgium.

The Korean research center KAIST has announced that they have found a way to produce PLA using bio-engineered Escherichia coli.[18]

Since 2009, Purac has developed a unique business model by starting production of Lactides (D and L, the monomers for PLA production, in their Spanish production plant with a capacity of several thousands of tons, while in March 2010 the construction has started of a 75.000 tons lactide plant at their production site in Thailand (Rayong Province). Purac has developed the technology to polymerize these lactides with Sulzer, a Swiss Engineering company. Purac collaborates with various PLA production partners to develop production scale and new markets for PLA. Thanks to the availability of D-lactide, Purac partners will be able to use stereo-complex technologies to produce new PLA grades with heat-stability (HDT) up to 180 degrees C, enabling use in higher value application area's. In a tripartite collaboration between Purac, Sulzer and Synbra solutions were developed to allow Synbra to start production of PLA and subsequently E-PLA, an attractive biodegradable and/or biobased alternative to EPS-foam in avariety of application areas. This collaboration was awarded by Frost and Sullivan with the Innovation of the Year Award in 2008 citing "This unique offering will significantly reduce the process and product development time enabling faster and more reliable market entry for PLA producers".

Recycling

In Belgium, Galactic started the first pilot unit to chemically recycle PLA (Loopla). Unlike mechanical recycling, waste material can hold various contaminants. Through thermal depolymerization, a highly purified lactic acid is extracted and can be considered as raw material for the manufacturing of virgin PLA with no loss of original properties (cradle-to-cradle recycling).

Recycling code

PLA has SPI resin ID code 7

Currently, SPI Resin identification code 7 is applicable. In 2007, a State Senate bill in California (SB 898)[19] proposed the marking of PLA with a new "0" code. However, this part of the bill was removed before passage.[20][21]

See also

References

  1. ^ Södergård, Anders; Mikael Stolt (February 2002). "Properties of lactic acid based polymers and their correlation with composition". Progress in Polymer Science 27 (6): 1123–1163. doi:10.1016/S0079-6700(02)00012-6. http://www.sciencedirect.com/science?_ob=ArticleURL&_udi=B6TX2-45JGY2J-4&_user=10&_coverDate=07%2F31%2F2002&_rdoc=1&_fmt=high&_orig=search&_sort=d&_docanchor=&view=c&_searchStrId=1423527891&_rerunOrigin=scholar.google&_acct=C000050221&_version=1&_urlVersion=0&_userid=10&md5=a26902c8a860132c06787a3727f61439. 
  2. ^ Middelton, John C.; Arthur J. Tipton (2000). "Synthetic biodegradable polymers as orthopedic devices". Biomaterial 21 (23): 2335–2346. doi:10.1016/S0142-9612(00)00101-0. http://www.sciencedirect.com/science?_ob=ArticleURL&_udi=B6TWB-418PMNJ-2&_user=10&_coverDate=12%2F01%2F2000&_rdoc=1&_fmt=high&_orig=search&_sort=d&_docanchor=&view=c&_searchStrId=1423528454&_rerunOrigin=scholar.google&_acct=C000050221&_version=1&_urlVersion=0&_userid=10&md5=9c513acdccd2530f1ac6ef005808cdbc. 
  3. ^ "High Tg Aliphatic Polyesters by the Polymerization of Spirolactide Derivatives". Polymer Chemistry. http://pollux.chem.umn.edu/publications/abstract306.html. 
  4. ^ "Compare Materials: PLA and PETE". Makeitfrom.com. http://www.makeitfrom.com/compare/?left=PLA&right=PET. Retrieved 2011-04-11. 
  5. ^ Lam, C. X. F.; Olkowski, R. .; Swieszkowski, W. .; Tan, K. C.; Gibson, I. .; Hutmacher, D. W. (2008). "Mechanical and in vitro evaluations of composite PLDLLA/TCP scaffolds for bone engineering". Virtual and Physical Prototyping 3 (4): 193–197. doi:10.1080/17452750802551298.  edit
  6. ^ Fiore, G; L.; Jing, F.; Young Jr., V. G.; Cramer, C. J.; Hillmyer, M. A. (2010). "High Tg Aliphatic Polyestersby the Polymerization o f Spir olactide Derivatives". Polym. Chem. (1): 870–877. 
  7. ^ "Bioengineers succeed in producing plastic without the use of fossil fuels". Physorg.com. http://www.physorg.com/news178178601.html. Retrieved 2011-04-11. 
  8. ^ Niță T (Feb 2011). "Concepts in biological analysis of resorbable materials in oro-maxillofacial surgery". Revista de Chirurgie Oro-Maxilo-Facială și Implantologie 2 (1): 33–38. http://www.revistaomf.ro/index.php?section=Article&ID=23. Retrieved 2011-03-12. 
  9. ^ Royte, Elizabeth (August 2006). "Corn Plastic to the Rescue". Smithsonian Magazine. http://www.smithsonianmag.com/science-nature/plastic.html. Retrieved 2008-03-06. 
  10. ^ "Toughened PLA". http://www.license.umn.edu/Products/Biodegradable-Polylactic-Acid-Plastic-is-Strengthened-with-Co-polymer__Z09084.aspx. Retrieved 27 May 2011. 
  11. ^ "Daily Bread is first to go green: News from Tristar". Manufacturingtalk.com. 2006-06-26. http://www.manufacturingtalk.com/news/trj/trj110.html. Retrieved 2011-04-11. 
  12. ^ "Home- Canada Green Natural Products". Cagreen.ca. http://www.cagreen.ca. Retrieved 2011-04-11. 
  13. ^ "Heat-Resistant Thermoplastic Made From Renewable, Biodegradable and Eco-Friendly Polymer PLA". University of Minnesota. http://www.license.umn.edu/Products/Heat-Resistant-Thermoplastic-Made-From-Renewable--Biodegradable-and-Eco-Friendly-Polymer-PLA__Z08149.aspx. Retrieved 26 May 2011. 
  14. ^ ""Tea Packaging for Impact and Sustainability" by Katrina Ávila Munichiello, ''Tea & Coffee Trade Journal''". Teaandcoffee.net. http://www.teaandcoffee.net/0909/tea.htm. Retrieved 2011-04-11. 
  15. ^ Kennedy, Ross. (2010). Pharmaceutics 2 - Module 2. CSU. Australia
  16. ^ "PLA". Reprap Wiki. 2011-04-04. http://reprap.org/wiki/PLA. Retrieved 2011-04-11. 
  17. ^ "PLA". MakerBot Industries. http://wiki.makerbot.com/pla. Retrieved 2011-04-11. 
  18. ^ "Koreans make plastics without fossil fuel chemicals". Edition.cnn.com. 2009-11-23. http://edition.cnn.com/2009/TECH/science/11/23/eco.korea.plastic/index.html. Retrieved 2011-04-11. 
  19. ^ "Full text and version history of California State Senate Bill 898". Leginfo.ca.gov. 2011-02-18. http://www.leginfo.ca.gov/cgi-bin/postquery?bill_number=sb_898&sess=CUR&house=B&author=simitian. Retrieved 2011-04-11. 
  20. ^ "Bill summary from Californians Against Waste, an environmental group". Cawrecycles.org. http://www.cawrecycles.org/issues/current_legislation/sb898_07. Retrieved 2011-04-11. 
  21. ^ Simitian. "SB 898 Senate Bill — AMENDED". Leginfo.ca.gov. http://www.leginfo.ca.gov/pub/07-08/bill/sen/sb_0851-0900/sb_898_bill_20070906_amended_asm_v95.html. Retrieved 2011-04-11. 

External links


Wikimedia Foundation. 2010.

Look at other dictionaries:

  • polylactic acid — noun A biodegradable thermoplastic made by polymerization of lactic acid residues …   Wiktionary

  • polylactic acid — poly·lac·tic ac·id (pol″e lakґtik) a hydrophobic hydroxy acid polymer that is formed into granules and used as a surgical dressing material for dental extraction sites, primarily for prevention of postoperative alveolar osteitis …   Medical dictionary

  • polylactic — adjective Of or pertaining to a polymer of lactic acid or its derivatives …   Wiktionary

  • Lactic acid — L Lactic acid …   Wikipedia

  • PLGA polylactic-glycolic acid — placental growth factor …   Medical dictionary

  • Bioplastic — This article is about plastics made from renewable biomass. For the information on plastics which are biodegradable, see biodegradable plastic. Biodegradable plastic utensils …   Wikipedia

  • Tissue engineering — Principle of tissue engineering Tissue engineering was once categorized as a sub field of bio materials, but having grown in scope and importance it can be considered as a field in its own right. It is the use of a combination of cells,… …   Wikipedia

  • Poly-Lactid — Sparschwein aus PLA Polylactide, die auch Polymilchsäuren (kurz PLA, vom englischen Wort polylactic acid) genannt werden, sind durch Wärmezufuhr verformbare Kunststoffe (siehe dazu Thermoplaste). Sie sind aus vielen, chemisch aneinander… …   Deutsch Wikipedia

  • Polylactat — Sparschwein aus PLA Polylactide, die auch Polymilchsäuren (kurz PLA, vom englischen Wort polylactic acid) genannt werden, sind durch Wärmezufuhr verformbare Kunststoffe (siehe dazu Thermoplaste). Sie sind aus vielen, chemisch aneinander… …   Deutsch Wikipedia

  • Polylactid — Sparschwein aus PLA Polylactide, die auch Polymilchsäuren (kurz PLA, vom englischen Wort polylactic acid) genannt werden, sind durch Wärmezufuhr verformbare Kunststoffe (siehe dazu Thermoplaste). Sie sind aus vielen, chemisch aneinander… …   Deutsch Wikipedia


Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”

We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.